Champagne Electrophoretic Frame Accessories , Solar Panel And Led
|Description||Champagne Electrophoretic Frame Accessories , Solar Panel And Led
|Material Thickness(t)||t=1.0 / 1.2 / 1.4|
|Material||Aluminum Alloy 6063, 6061|
|Color||Green, Grey, Black, White, (RAL series)etc.|
Mill finish, anodized, powder coated, electrophoresis,
sand balsting etc.and depend on customer’s demand.
|Shape||Square, Round, Flat, Oval, and according to customer's drawing.|
|Length||Normal length=6m or in customer's order|
Building, Production Line, Decoration, Industrial, Transportation,
Door and window, etc.
1. Pearl cotton foam for each profile;
2. Wrap with shrink film exterior;
3. Packed according to customer request.
Providing colorful products with various mechanical
performances to adapt all kinds of architectural styles
Organic silane treatment
Organosilylation is a new kind of metal surface protection
technology developed in recent years. Due to the non-pollution and
the treatment of the durable corrosion, it is favored by people.
The process is based on a silane reagent based on hydrolysis.
Organic silane class and basal aluminum alloy forming strong Me - O
- Si keys, and the organic part of the silane and polymer coating
and surface (primer) form the etch primer processing chemical
bonds, the formation of siloxane bonding can greatly improve the
adhesion strength of the polymer coating and matrix aluminum alloy
surface, and at the same time to improve the corrosion resistance
of aluminum alloy.
Silane treated traditionally dip coating process, the aluminum
alloy immersed in this rare silane solution in a certain time, then
curing under a certain temperature, can be formed in the aluminum
alloy surface hundreds of meters thick coating (curing than
traditional transition coating thin), the coating can effectively
prevent various forms of corrosion in aluminum alloy. The DTMS
membrane was prepared by electrochemical technique on the surface
deposition of LY12 aluminum alloy. The reflective absorption
spectra indicates that the DTMS silane reagent has a chemical bond
cooperation with the aluminum alloy substrate surface, and the
SiOAl bond is formed into the membrane. The test result of
electrochemical impedance spectroscopy (EIS) shows that the
corrosion resistance of silane film with cathode potential
deposition is improved obviously compared with that of open-circuit